===Disposable===
===Disposable===
====Zinc–Carbon====
====Zinc–Carbon====
[[File:Baterija 3336 USSR.jpg|thumb|upright|A USSR-manufactured 4.5V zinc–carbon battery from 1981]]
Zinc–carbon was the first commercially available battery type and is still somewhat frequently used, although it has largely been replaced by the similarly composed alkaline battery. Like the alkaline battery, the zinc–carbon battery contains manganese dioxide and zinc electrodes. Unlike the alkaline battery, the zinc–carbon battery uses ammonium chloride as the electrolyte (zinc chloride in the case of "heavy-duty" zinc–carbon batteries), which is acidic.
Zinc–carbon was the first commercially available battery type and is still somewhat frequently used, although it has largely been replaced by the similarly composed alkaline battery. Like the alkaline battery, the zinc–carbon battery contains manganese dioxide and zinc electrodes. Unlike the alkaline battery, the zinc–carbon battery uses ammonium chloride as the electrolyte (zinc chloride in the case of "heavy-duty" zinc–carbon batteries), which is acidic.


Line 15: Line 16:


====Alkaline====
====Alkaline====
[[File:Alkaline battery (leaked) 1.jpg|thumb|upright=0.5|A leaking AA alkaline battery]]
Alkaline batteries use manganese dioxide and zinc electrodes with an electrolyte of potassium hydroxide. The alkaline battery gets its name from the replacement of the acidic ammonium chloride of zinc–carbon batteries with potassium hydroxide, which is an alkaline. Alkaline batteries are considerably more efficient, more environmentally friendly, and more shelf-stable than zinc–carbon batteries—five to ten years, when stored room temperature.<ref name=energizer /> Alkaline batteries largely replaced zinc-carbon batteries in regular use by 1990.<ref>Holusha, Josh (June 3, 1990). [https://www.nytimes.com/1990/06/03/business/technology-trying-to-make-batteries-green.html "Trying to Make Batteries 'Green'"]. ''The New York Times''.</ref>
Alkaline batteries use manganese dioxide and zinc electrodes with an electrolyte of potassium hydroxide. The alkaline battery gets its name from the replacement of the acidic ammonium chloride of zinc–carbon batteries with potassium hydroxide, which is an alkaline. Alkaline batteries are considerably more efficient, more environmentally friendly, and more shelf-stable than zinc–carbon batteries—five to ten years, when stored room temperature.<ref name=energizer /> Alkaline batteries largely replaced zinc-carbon batteries in regular use by 1990.<ref>Holusha, Josh (June 3, 1990). [https://www.nytimes.com/1990/06/03/business/technology-trying-to-make-batteries-green.html "Trying to Make Batteries 'Green'"]. ''The New York Times''.</ref>


Line 20: Line 22:


Alkaline battery leakage can be effectively neutralized with lemon juice or distilled white vinegar. Eye protection and rubber gloves should be worn, as the potassium hydroxide electrolyte is caustic.<ref>[https://www.upsbatterycenter.com/blog/clean-alkaline-battery-leaks/ "How to Clean Up Alkaline Battery Leaks".] UPS Battery Center. January 14, 2017.</ref>
Alkaline battery leakage can be effectively neutralized with lemon juice or distilled white vinegar. Eye protection and rubber gloves should be worn, as the potassium hydroxide electrolyte is caustic.<ref>[https://www.upsbatterycenter.com/blog/clean-alkaline-battery-leaks/ "How to Clean Up Alkaline Battery Leaks".] UPS Battery Center. January 14, 2017.</ref>
====Lithium====
[[File:LeakedBattery 2585a.jpg|thumb|upright=0.5|A leaking lithium button cell]]
Non-rechargeable lithium batteries have a metallic lithium anode and assorted metallic compounds as cathodes—usually manganese dioxide—with a an electrolyte of lithium salt dissolved in solvent.
A common form of these non-rechargeable lithium batteries are button cells, as used in watches, calculators and motherboard batteries since the mid-1990s.
One of the first personal computers with a built-in lithium battery was the original Macintosh from 1984. Its battery was used for the purposes of preserving the contents of Parameter RAM (PRAM)—Apple's analogue to the BIOS of the IBM PC. The first iterations of the Macintosh stored the battery in a clip-on compartment in the back, allowing it to be replaced by the end user.<ref>[https://www.ifixit.com/Teardown/Macintosh+128K+Teardown/21422 "Macintosh 128K Teardown"]. iFixit.</ref> Later iterations (from the Macintosh II onward) put the battery either in a metal compartment on the surface of the logic board, with a plastic shell to hold it in, or had the battery soldered directly to pads on the logic board, in a form similar to an axial [[capacitor]]. Apple used three brands of lithium batteries for this PRAM application from the 1980s to the early 2000s: Tadiran, Varta, and Maxell. The latter Maxell batteries are nicknamed "red bombs" due to their tendency to rupture violently, causing irreparable damage and corrosion to all components and traces in its vicinity.<ref>[https://68kmla.org/bb/index.php?threads/warning-exploding-maxell-pram-batteries.25169/ "Warning! Exploding Maxell PRAM Batteries"]. 68kMLA.</ref><ref>[https://www.reddit.com/r/VintageApple/comments/kpqaof/i_picked_up_a_classic_today_and_it_had_a_maxell/ "I picked up a Classic today, and it had a Maxell battery explosion ..."] Reddit.</ref><ref>[https://applerescueofdenver.com/news/ "Remove your PRAM Batteries!"] Apple Rescue of Denver.</ref>


===Rechargable===
===Rechargable===
====Nickel–Cadmium (Ni-Cd)====
====Nickel–Cadmium (Ni-Cd)====
Nickel–cadmium batteries use nickel oxide hydroxide and metallic cadmium electrodes with an electrolyte of potassium hydroxide.
Nickel–cadmium batteries use nickel oxide hydroxide and metallic cadmium electrodes with an electrolyte of potassium hydroxide. Sealed Ni-Cd batteries were widely used in photography equipment, handheld power tools, and radio-controlled toys from the early 1940s until the early 1990s, when nickel–metal hydride batteries supplanted them (like how alkaline batteries replaced zinc–carbon batteries). In computers, Ni-Cd batteries first saw use in the mid-1980s as a cheaper alternative to lithium batteries for powering real-time clocks and preserving BIOS settings. Nickel–cadmium batteries were also briefly used in laptop battery packs, until the advent of commercially viable nickel–metal hydride batteries in the early 1990s.<ref name=pcmag>O'Brien, Bill (March 12, 1991). [https://books.google.com/books?id=GF_6VuE4h2MC&pg=PT116 "Nickel Metal-Hydride: A Kinder, Gentler Battery"]. ''PC Magazine''.</ref> Ni-Cd batteries are still used in some uninterruptible power supplies and emergency lighting setups.
 
Except in aeronautical or other high-risk applications, Ni-Cd batteries are intentionally not hermetically sealed and include pressure vents for safety if the batteries are charged improperly. With age and sufficient thermal cycles the seal will degrade and allow electrolyte to leak through.<ref>[https://digitalcommons.usu.edu/cgi/viewcontent.cgi?article=2815&context=smallsat "Utilization of Small Commercial Grade Nickel Cadmium (NiCd) Cells in Low Earth Orbit (LEO) Applications"]. Utah State University. August 1990.</ref> The leakage usually travels down the positive and/or negative terminals onto any surrounding circuitry (see the [[#top|top image]]).
 
Like with alkaline battery leakage, Ni-Cd leakage can be effectively neutralized with lemon juice or distilled white vinegar.


====Nickel–Metal Hydride (Ni-MH)====
====Nickel–Metal Hydride (Ni-MH)====
Nickel–metal hydride (Ni-MH) largely replaced Ni-Cd batteries in the early 1990s.<ref name=pcmag /> They replaced the metallic cadmium electrode with a hydrogen-absorbing alloy, allowing it to have over two times the capacity of Ni-Cd batteries while being easier to recycle. Their heyday in computer equipment was in the early- to mid-1990s. By 1995, most motherboard manufacturers switched to non-rechargable lithium button cells to keep the BIOS chip powered.<ref>Bigelow, Stephen J. (1994) [https://www.google.com/books/edition/Troubleshooting_and_Repairing_Notebook_P/BYNTAAAAMAAJ?gbpv=1&bsq=motherboard+lithium+coin+cell ''Troubleshooting and Repairing Notebook, Palmtop, and Pen Computers'']. p. 20. ISBN 9780070052406.</ref> Lithium-based battery packs replaced Ni-MH packs in all but the lowest-end laptops by the early 2000s.<ref>Mueller, Scott (2004). [https://www.google.com/books/edition/Upgrading_and_Repairing_Laptops/xCXVGneKwScC?hl=en&gbpv=1&pg=PA255&printsec=frontcover ''Upgrading and Repairing Laptops'']. p. 255. ISBN 9780789728005.</ref>
The practical shelf life of a Ni-MH is roughly five years. Cylindrical jelly-roll Ni-MH cells, like the ones used in 1990s laptop battery packs, discharge at a rate of up to 2% per day, while button cells like the ones used in motherboard batteries discharge at a rate of less than 20% per month.<ref>[https://www.master-instruments.com.au/pages/battery-shelf-life-storage.html "Battery Shelf Life & Storage"]. Master Instruments.</ref> They are said to leak less frequently than alkaline batteries but have a similar failure mode.<ref>[https://www.grepow.com/blog/do-nimh-batteries-explode/ "Do NiMH Batteries Explode?"] Grepow Blog.</ref>
Ni-MH leakage can be effectively neutralized with lemon juice or distilled white vinegar.
====Lithium-Ion====
[[File:18650-leak-1.jpg|thumb|upright=0.5|A leaking 18650 Li-Ion cell]]
{{Wikipedia|Lithium-ion battery}}
From Wikipedia:
: A lithium-ion battery ... is a type of rechargeable battery in which lithium ions move from the negative electrode through an electrolyte to the positive electrode during discharge and back when charging. Li-ion batteries use an intercalated lithium compound as the material at the positive electrode and typically graphite at the negative electrode.<ref>[https://en.wikipedia.org/wiki/Lithium-ion_battery "Lithium-ion battery"]. Wikipedia. Retrieved February 15, 2022.</ref>
: If overheated or overcharged, Li-ion batteries may suffer thermal runaway and cell rupture. In extreme cases this can lead to leakage, explosion or fire. To reduce these risks, many lithium-ion cells (and battery packs) contain fail-safe circuitry that disconnects the battery when its voltage is outside the safe range of 3–4.2 V per cell ...


'''Lead Acid'''


====Lithium====
Lead acid batteries were the first rechargable battery. Their perfomance is a lot lower compared to modern alternatives such as Ni-MH and Lithium ion. Despite their lower capacity and significant weight, they are able to supply a large amount of current which is why they are still used in stationary applications, and where weight and capacity is not as much of a concern. E.G. ICE Vehicles, Uninteruptible Power Supplies.
 
A single lead acid cell is nominally 2.1v when charged. A car battery being comprised of 6 of these cells connected in series to form a 12V battery. (12.6v nominally, however when charging you will see up to 14.5v, and when discharged as low as 10v)
 
 
They contain Sulphuric Acid, so any contact with skin needs to be washed immediatly, and you should be mindful that they contain lead as well. They are able to be float charged permanatly, for example in a uninteruptible power supply, however after ~5 years of being on charge even sealed versions (SLA, AGM) will have their electrolyte evaporate, this can cause them to swell over time which can cause them to crack and leak.




===="Dallas"====
If left for a couple of years without charging, they will discharge and the plates will become coated in lead sulphate. This is known as "Sulphation" and it will reduce the capacity / usability of it.


==References==
==References==

Latest revision as of 17:42, 6 May 2023

For more information, see this article's corresponding Wikipedia page: Electric battery.
A nickel–cadmium Varta barrel battery that has leaked onto the mainboard of a Korg Poly-61, causing massive corrosion to circuit board traces and legs of integrated circuits.

A battery is a self-contained device that converts chemical chemical energy into a direct current by way of a redox reaction. It consists of one or more cells, the composition of which determines whether the battery is disposable (primary) or rechargeable (secondary). Batteries are typically opposed to mains power as a source of electrical energy, although the two are often used in tandem to power components within a piece of equipment.

In the context of repairing equipment, batteries can be problematic due to their propensity for leaking.

Battery Types and Risks

Disposable

Zinc–Carbon

A USSR-manufactured 4.5V zinc–carbon battery from 1981

Zinc–carbon was the first commercially available battery type and is still somewhat frequently used, although it has largely been replaced by the similarly composed alkaline battery. Like the alkaline battery, the zinc–carbon battery contains manganese dioxide and zinc electrodes. Unlike the alkaline battery, the zinc–carbon battery uses ammonium chloride as the electrolyte (zinc chloride in the case of "heavy-duty" zinc–carbon batteries), which is acidic.

Either when it has been completely consumed or after three to five years from its manufacture (its shelf life),[1] a zinc–carbon battery is prone to leaking. The contents of the leakage may include manganese hydroxide, zinc ammonium chloride, ammonia, zinc chloride, zinc oxide, water and starch. None of these are particularly dangerous to human skin, but this combination of materials is corrosive to metals, such as those of the battery contacts and surrounding circuitry.[2]

Online discussions suggest that zinc-carbon battery leakage can be effectively cleaned with baking soda.[3]

Alkaline

A leaking AA alkaline battery

Alkaline batteries use manganese dioxide and zinc electrodes with an electrolyte of potassium hydroxide. The alkaline battery gets its name from the replacement of the acidic ammonium chloride of zinc–carbon batteries with potassium hydroxide, which is an alkaline. Alkaline batteries are considerably more efficient, more environmentally friendly, and more shelf-stable than zinc–carbon batteries—five to ten years, when stored room temperature.[1] Alkaline batteries largely replaced zinc-carbon batteries in regular use by 1990.[4]

After an alkaline battery has been spent, or as it reaches the ends of its shelf life, the chemistry of its cells change, and hydrogen gas is generated as a byproduct. When enough pressure has been built up internally, the casing splits at the bases or side (or both), releasing manganese oxide, zinc oxide, potassium hydroxide, zinc hydroxide, and manganese hydroxide.[2]

Alkaline battery leakage can be effectively neutralized with lemon juice or distilled white vinegar. Eye protection and rubber gloves should be worn, as the potassium hydroxide electrolyte is caustic.[5]

Lithium

A leaking lithium button cell

Non-rechargeable lithium batteries have a metallic lithium anode and assorted metallic compounds as cathodes—usually manganese dioxide—with a an electrolyte of lithium salt dissolved in solvent.

A common form of these non-rechargeable lithium batteries are button cells, as used in watches, calculators and motherboard batteries since the mid-1990s.

One of the first personal computers with a built-in lithium battery was the original Macintosh from 1984. Its battery was used for the purposes of preserving the contents of Parameter RAM (PRAM)—Apple's analogue to the BIOS of the IBM PC. The first iterations of the Macintosh stored the battery in a clip-on compartment in the back, allowing it to be replaced by the end user.[6] Later iterations (from the Macintosh II onward) put the battery either in a metal compartment on the surface of the logic board, with a plastic shell to hold it in, or had the battery soldered directly to pads on the logic board, in a form similar to an axial capacitor. Apple used three brands of lithium batteries for this PRAM application from the 1980s to the early 2000s: Tadiran, Varta, and Maxell. The latter Maxell batteries are nicknamed "red bombs" due to their tendency to rupture violently, causing irreparable damage and corrosion to all components and traces in its vicinity.[7][8][9]

Rechargable

Nickel–Cadmium (Ni-Cd)

Nickel–cadmium batteries use nickel oxide hydroxide and metallic cadmium electrodes with an electrolyte of potassium hydroxide. Sealed Ni-Cd batteries were widely used in photography equipment, handheld power tools, and radio-controlled toys from the early 1940s until the early 1990s, when nickel–metal hydride batteries supplanted them (like how alkaline batteries replaced zinc–carbon batteries). In computers, Ni-Cd batteries first saw use in the mid-1980s as a cheaper alternative to lithium batteries for powering real-time clocks and preserving BIOS settings. Nickel–cadmium batteries were also briefly used in laptop battery packs, until the advent of commercially viable nickel–metal hydride batteries in the early 1990s.[10] Ni-Cd batteries are still used in some uninterruptible power supplies and emergency lighting setups.

Except in aeronautical or other high-risk applications, Ni-Cd batteries are intentionally not hermetically sealed and include pressure vents for safety if the batteries are charged improperly. With age and sufficient thermal cycles the seal will degrade and allow electrolyte to leak through.[11] The leakage usually travels down the positive and/or negative terminals onto any surrounding circuitry (see the top image).

Like with alkaline battery leakage, Ni-Cd leakage can be effectively neutralized with lemon juice or distilled white vinegar.

Nickel–Metal Hydride (Ni-MH)

Nickel–metal hydride (Ni-MH) largely replaced Ni-Cd batteries in the early 1990s.[10] They replaced the metallic cadmium electrode with a hydrogen-absorbing alloy, allowing it to have over two times the capacity of Ni-Cd batteries while being easier to recycle. Their heyday in computer equipment was in the early- to mid-1990s. By 1995, most motherboard manufacturers switched to non-rechargable lithium button cells to keep the BIOS chip powered.[12] Lithium-based battery packs replaced Ni-MH packs in all but the lowest-end laptops by the early 2000s.[13]

The practical shelf life of a Ni-MH is roughly five years. Cylindrical jelly-roll Ni-MH cells, like the ones used in 1990s laptop battery packs, discharge at a rate of up to 2% per day, while button cells like the ones used in motherboard batteries discharge at a rate of less than 20% per month.[14] They are said to leak less frequently than alkaline batteries but have a similar failure mode.[15]

Ni-MH leakage can be effectively neutralized with lemon juice or distilled white vinegar.

Lithium-Ion

A leaking 18650 Li-Ion cell
For more information, see this article's corresponding Wikipedia page: Lithium-ion battery.

From Wikipedia:

A lithium-ion battery ... is a type of rechargeable battery in which lithium ions move from the negative electrode through an electrolyte to the positive electrode during discharge and back when charging. Li-ion batteries use an intercalated lithium compound as the material at the positive electrode and typically graphite at the negative electrode.[16]
If overheated or overcharged, Li-ion batteries may suffer thermal runaway and cell rupture. In extreme cases this can lead to leakage, explosion or fire. To reduce these risks, many lithium-ion cells (and battery packs) contain fail-safe circuitry that disconnects the battery when its voltage is outside the safe range of 3–4.2 V per cell ...


Lead Acid

Lead acid batteries were the first rechargable battery. Their perfomance is a lot lower compared to modern alternatives such as Ni-MH and Lithium ion. Despite their lower capacity and significant weight, they are able to supply a large amount of current which is why they are still used in stationary applications, and where weight and capacity is not as much of a concern. E.G. ICE Vehicles, Uninteruptible Power Supplies.

A single lead acid cell is nominally 2.1v when charged. A car battery being comprised of 6 of these cells connected in series to form a 12V battery. (12.6v nominally, however when charging you will see up to 14.5v, and when discharged as low as 10v)


They contain Sulphuric Acid, so any contact with skin needs to be washed immediatly, and you should be mindful that they contain lead as well. They are able to be float charged permanatly, for example in a uninteruptible power supply, however after ~5 years of being on charge even sealed versions (SLA, AGM) will have their electrolyte evaporate, this can cause them to swell over time which can cause them to crack and leak.


If left for a couple of years without charging, they will discharge and the plates will become coated in lead sulphate. This is known as "Sulphation" and it will reduce the capacity / usability of it.